Etp Copper Wire Rod for Cable

Our ETP copper wire rod for cable is made specifically for the cable manufacturing industry. The product design starts with one question. How does the rod perform on a drawing machine? Our customers care about breakage rates.
Send Inquiry
Description

Engineered for High-Speed Drawing Performance

 

Our ETP copper wire rod for cable is made specifically for the cable manufacturing industry. The product design starts with one question. How does the rod perform on a drawing machine? Our customers care about breakage rates. They care about drawing speed. They care about finished wire quality. We have optimized our production for these factors. The oxygen content stays within a range that supports smooth drawing. This gives a practical balance between conductivity and processability. Our customers report consistent performance on their equipment. The breakage rate stays low. This reduces downtime and material waste. Our team performs regular twist tests during production. If the rod cracks during twisting, it indicates internal problems. This simple test helps us catch issues early.

 

The Twist Test and Quality Monitoring

 

The twist test is a reliable indicator of rod quality. We take samples regularly and twist them until they break. The break pattern tells us about internal structure. A clean, ductile break indicates good material. A brittle, jagged break indicates problems. Our workers have learned to read these signs accurately. They also monitor the rod surface for scale or pits. Surface defects cause breaks during drawing. We reject any material that shows issues. We also track breakage rates from customer feedback. This data helps us refine our process. Our goal is continuous improvement in drawing performance. We also monitor the oxide layer thickness. Too much oxide affects drawing. Too little oxide may indicate other issues.

Size Options and Technical Data

 

We stock this rod in 16mm and 20mm diameters. The material is T2 copper. Production follows GB/T5585.1-2026. Copper purity reaches Cu≥99.90%. Total impurities stay below 0.10%. Conductivity is ≥97.3% IACS. Resistivity at 20°C stays ≤0.0177 Ω·mm²/m. Density is 8.9 g/cm³. Tensile strength ranges from 220 to 260 MPa. Yield strength exceeds 170 MPa. Hardness is 65 to 90 HV. Elongation is 17% or higher.

Built for Cable Factory Efficiency

 

ETP copper wire rod for cable serves the cable industry directly. The product supports high drawing speeds. This increases factory output. The low breakage rate reduces waste. This lowers production costs. The rod also produces consistent wire quality. This reduces quality control rejections. Our customers include major cable factories. Export sales continue to grow. The product has proven itself in demanding production environments. Cable makers trust it for their daily operations. The consistent quality helps them maintain their own customer satisfaction. We ship globally to cable manufacturers who value reliability.

Order and Production Information

 

We keep raw materials in stock. This allows fast order fulfillment. Standard sizes ship within one week. We also handle custom requirements. The minimum order is 1000 kilograms. Mixed specifications in one order are accepted. We welcome third-party inspection. Our team processes orders efficiently. The production line runs on a steady schedule. We accept USD, EUR, and CNY for settlement.

Technical Parameters

 

 

Parameter

Value

Material Grade

T2 Copper (Cable-Grade Low Oxygen)

Copper Purity

Cu≥99.90%

Standard

GB/T5585.1-2026

Electrical Conductivity

≥97.3% IACS

Resistivity (20°C)

≤0.0177 Ω·mm²/m

Density

8.9 g/cm³

Tensile Strength

220–260 MPa

Yield Strength

≥170 MPa

Hardness

65–90 HV

Elongation

≥17%

Stock Sizes

16mm, 20mm

 

Hot Tags: etp copper wire rod for cable, China etp copper wire rod for cable manufacturers, suppliers, factory